Y. Li, X. D. Cheng, W. Cao, L. L. Gong, R. F. Zhang and H. P. Zhang (2015) Materials & Design 88 1008-1014.
Date: 2016-02-29   Author: SKLFS  ,   Source: SKLFS  ,
 

Y. Li, X. D. Cheng, W. Cao, L. L. Gong, R. F. Zhang and H. P. Zhang (2015) Fabrication of adiabatic foam at low temperature with sodium silicate as raw material. Journal/Materials &, Design 88 1008-1014. [In English]
Web link: http://dx.doi.org/10.1016/j.matdes.2015.09.078
Keywords: Adiabatic foam, Low temperature, Thermal conductivity, Density, Compression strength, ASH-BASED GEOPOLYMER, LOW THERMAL-CONDUCTIVITY, FLY-ASH, PHYSICAL-PROPERTIES, GLASS, INSULATION, SPECTROSCOPY, CERAMICS, PRESSURE, MORTAR
Abstract: The process of adiabatic foam, fabricated at low temperature, is described in this research using sodium silicate as the raw material. Fly ash was added to increase the strength of the samples to guarantee the needs of thermal insulation material application. The thermal conductivity, density, compression strength and microstructure were characterized in this paper. The results show that the sintering process, fly ash content and modulus of sodium silicate greatly affected the above properties. Samples with 0.0488 W/m K of thermal conductivity, 97 kg/m(3) of density and 0.44 MPa of compression strength were obtained. Therefore, this adiabatic foam has a large potential of insulation application. (C) 2015 Published by Elsevier Ltd.

 ,

 
Print    Close
 
 
   
  
 
Relevant link
Contact us
State Key Laboratory of Fire Science, University of Science and Technology of China
Jinzhai Road 96, Hefei, Anhui, P. R. China
P. O.: 230026
   
Tel:(+86)551 63601651
Fax:(+86)551 63601669
E-mail:sklfs@ustc.edu.cn
 
 
Copyright © 1990-2011 State Key Laboratory of Fire Science, University of Science and Technology of China
Tel:(+86)551 3601651 | Fax:(+86)551 3601669 | E-mail:sklfs@ustc.edu.cn | ICP: D20380176