Y. Y. Han, J. X. Yi and X. Guo (2014) Improving the chemical stability of oxygen permeable SrFeO3-delta perovskite in CO2 by niobium doping. Journal/Solid State Ionics 267 44-48. [In English] Web link: http://dx.doi.org/10.1016/j.ssi.2014.09.009 Keywords: ,Perovskite, Mixed conductor, CO2, Stability, Oxygen separation, PHASE-STABILITY, MEMBRANES, PERMEATION, CO2-TOLERANT, SEPARATION, BEHAVIOR Abstract: Among mixed-conducting perovskite oxides, SrFeO3 - delta shows very good oxygen permeability, but it suffers degradation in the presence of CO2. In this work, we investigated the effects of Nb doping on the structure and oxygen permeability of SrFe1 - xNb2O3 - delta (x = 0-0.30). For SrFeO3 - delta, significant absorption of and reaction with CO2 led to structural degradation as well as rapid deterioration of the oxygen permeation flux at 800 degrees C. However, the reaction became much less pronounced and the decrease of the flux was much smaller with Nb doping (x = 0.05-0.20). Most importantly, almost no reaction and no decrease in the oxygen flux were observed even at the relatively low temperature of 800 degrees C as the Nb doping was increased to 0.3. The improvement of the CO2 resistance with Nb doping was discussed in terms of the increased metal-oxygen bonding in the perovskite. (C) 2014 Elsevier B.V. All rights reserved.
|
|
|
|
|
|
|
|
|
|
![](/_upload/tpl/00/6b/107/template107/res/Contactus_b01.gif) |
State Key Laboratory of Fire Science, University of Science and Technology of China
Jinzhai Road 96, Hefei, Anhui, P. R. China
P. O.: 230026 |
|
|
![](/_upload/tpl/00/6b/107/template107/res/Contactus_b02.gif) |
Tel:(+86)551 63601651 |
![](/_upload/tpl/00/6b/107/template107/res/Contactus_b03.gif) |
Fax:(+86)551 63601669 |
![](/_upload/tpl/00/6b/107/template107/res/Contactus_b04.gif) |
E-mail:sklfs@ustc.edu.cn |
|
|
|
|
|