H. R. Qian, X. D. Cheng, H. P. Zhang, R. F. Zhang and Y. H. Wang (2014) International Journal Of Applied Ceramic Technology 11 858-863.
Date: 2015-03-28   Author: SKLFS  ,   Source: SKLFS  ,
 

H. R. Qian, X. D. Cheng, H. P. Zhang, R. F. Zhang and Y. H. Wang (2014) International Journal Of Applied Ceramic Technology 11 858-863.

Web link: http://dx.doi.org/10.1111/ijac.12204
Keywords: FABRICATION, COMPOSITES

Abstract: Porous mullite ceramics were fabricated from an industrial grade mullite powder by gelcasting process using fly ash cenospheres (FAC) as a pore-forming agent. The influence of content of FAC and sintering temperature on the density and strength was evaluated. The microstructure showed that FAC can act as a sintering aid and a pore-forming agent. When the sintering temperature at 1200 degrees C, porous mullite ceramics with a relatively high porosity (48.1-72.2%), low density (0.84-1.64 g/cm(3)), low thermal conductivity (0.16-0.22 W/m . K), and high compressive strength (6.21-14.70 MPa) have been obtained.

 
Print    Close
 
 
   
  
 
Relevant link
Contact us
State Key Laboratory of Fire Science, University of Science and Technology of China
Jinzhai Road 96, Hefei, Anhui, P. R. China
P. O.: 230026
   
Tel:(+86)551 63601651
Fax:(+86)551 63601669
E-mail:sklfs@ustc.edu.cn
 
 
Copyright © 1990-2011 State Key Laboratory of Fire Science, University of Science and Technology of China
Tel:(+86)551 3601651 | Fax:(+86)551 3601669 | E-mail:sklfs@ustc.edu.cn | ICP: D20380176